HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA

HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA

    • HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA
    • HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA
  • HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA

    Product Details:

    Place of Origin: Jiangsu / China
    Brand Name: HTTM
    Certification: ISO 9001 : 2008
    Model Number: HF06U

    Payment & Shipping Terms:

    Minimum Order Quantity: 150 kg
    Price: Negotiable
    Packaging Details: Packed in plastic box first, and then stashed in a cardboard box, and finally reinforced with wooden boxes for outer packing
    Delivery Time: 14 days after full payment is received
    Payment Terms: T/T, Western Union
    Supply Ability: 20 tons per month
    Contact Now
    Detailed Product Description
    ISO - Range: K05 - K10 Size: Unground Fixed Length
    Hardness(HRA): 94.5 Density(g / Cm 3): 14.80
    WC(%): 94 Cobalt Content(%): 6
    TRS(MPa): >3500 Applications: Carbide Cutting Tools

    HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA

     


    Description: 

     

    Cemented carbide essentially consists of two main components: hard metal tungsten carbide (WC) and binding agent Co. Carbide contributes to high hardness property in a most important degree for hard metal WC, while cobalt maintains its relative high toughness at the high level of hardness. With Hot Isostatic Pressing sintering technique, cemented carbide material is fully consolidated by simultaneous application of heat and pressure, producing a close-to-full-density state. Consequently, the technique greatly optimizes rod’s quality, being more stable and reliable. 

     

    - ISO Range: K05-K10

     

    - with 94% tungsten carbide, 6% cobalt 

     

    - Made of 0.4 micron ultrafine TC powder

     

    - Hardness: 94.5 HRA

     

    - Bending strength: >3500 MPa

     

    - Density: 14.80 g/cm3

     

    - As sintered
                                                
    - Dimension: unground fixed length bar in metric size


     

    Specifications:

     

    HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA
     

    Solid rods- cut to length(Metric):

     

    D

    Tolerance of D

    Length

    D

    Tolerance of D

    Length

    mm

    (mm)

    mm

    mm

    (mm)

    mm

    3.0

    +0.2/+0.4

    38.5

    8.0

    +0.2/+0.4

    100

    3.0

    +0.2/+0.4

    50

    8.0

    +0.2/+0.4

    150

    3.0

    +0.2/+0.4

    60

    9.0

    +0.2/+0.4

    100

    3.0

    +0.2/+0.4

    75

    10.0

    +0.2/+0.4

    75

    3.0

    +0.2/+0.4

    100

    10.0

    +0.2/+0.4

    120

    4.0

    +0.2/+0.4

    50

    10.0

    +0.2/+0.4

    150

    4.0

    +0.2/+0.4

    60

    10.0

    +0.2/+0.4

    200

    4.0

    +0.2/+0.4

    75

    11.0

    +0.2/+0.4

    100

    4.0

    +0.2/+0.4

    100

    12.0

    +0.2/+0.4

    75

    5.0

    +0.2/+0.4

    50

    12.0

    +0.2/+0.4

    100

    5.0

    +0.2/+0.4

    60

    12.0

    +0.2/+0.4

    120

    5.0

    +0.2/+0.4

    75

    12.0

    +0.2/+0.4

    150

    5.0

    +0.2/+0.4

    100

    14.0

    +0.2/+0.4

    75

    6.0

    +0.2/+0.4

    50

    14.0

    +0.2/+0.4

    150

    6.0

    +0.2/+0.4

    75

    16.0

    +0.2/+0.4

    100

    6.0

    +0.2/+0.4

    100

    16.0

    +0.2/+0.4

    150

    6.0

    +0.2/+0.4

    150

    18.0

    +0.2/+0.4

    100

    6.0

    +0.2/+0.4

    60

    20.0

    +0.2/+0.4

    100

    8.0

    +0.2/+0.4

    75

    20.0

    +0.2/+0.4

    150

     
     HF06U / K05 - K10 Tungsten Carbide Rod Blanks with 6% Cobalt, Hardness 94.5 HRA


     

    Areas of Application:

     

    We would be glad to advise you when choosing the grades to suit optimally your requirements. Following are applications that our HF06U fits for cutting. 


    1. Grey cast Iron
    2. Unalloyed steels
    3. Plastic

     

     

    Competitive Advantage:

     

    Compared to high speed steel, tungsten carbide consists of natural hard and stable phase, and practically doesn’t lose any level of its high hardness when heating up. However, the high hardness of HSS is only in a result of quenching process during which hard phase nucleates & grows. It breaks down easily when annealing. Therefore, carbide tools last significantly longer than HSS.  
        
    Quality can be taken for granted. We have been producing tungsten powder, tungsten carbide powder FOR 11 years, being famous for its quality and winning high reputation within China. As so, each pre-process for making solid rods is clearly and strictly monitored. Thus, the quality of solid TC rods is guaranteed to be high and stable. 

    Contact Details
    Jiangsu Hetian Technological Material Co., Ltd.

    Contact Person: Miss. Voyonna. T

    Tel: 86-510-87490565

    Fax: 86-510-87492585

    Send your inquiry directly to us (0 / 3000)